UHP 550mm Graphite Electrode
Zane-zane mataki ne mai mahimmanci a cikin samar da lantarki mai graphite UHP.Yana nufin tsarin kula da zafi mai zafi na samfuran carbon sama da 2300 ℃ a cikin tanderun wutar lantarki mai zafin gaske don canza tsarin ƙirar ƙirar amorphous a cikin tsari mai girma uku da aka ba da umarni.
Menene aikin graphitization?
* Inganta wutar lantarki da yanayin zafi
* Haɓaka juriya na girgiza zafin zafi da kwanciyar hankali na sinadarai (ana rage ƙimar faɗaɗa layin layi da 50-80%);
* Sanya kayan carbon su sami mai mai da juriya;
* Fitar da ƙazanta da haɓaka tsabtar kayan carbon (an rage ash abun cikin samfurin daga 0.5% zuwa kusan 0.3%).
| Kwatanta Bayanin Fasaha don UHP Graphite Electrode 22" | ||
| Electrode | ||
| Abu | Naúrar | Specific mai bayarwa |
| Halayen Halayen Sanda | ||
| Diamita na Suna | mm | 550 |
| Max Diamita | mm | 562 |
| Min Diamita | mm | 556 |
| Tsawon Suna | mm | 1800-2400 |
| Matsakaicin Tsayin | mm | 1900-2500 |
| Min Tsawon | mm | 1700-2300 |
| Yawan yawa | g/cm3 | 1.68-1.72 |
| Ƙarfin mai juzu'i | MPa | ≥ 12.0 |
| Young' Modul | GPA | ≤13.0 |
| Takamaiman Juriya | µΩm | 4.5-5.6 |
| Matsakaicin yawa na yanzu | KA/cm2 | 18-27 |
| Ƙarfin ɗauka na Yanzu | A | 45000-65000 |
| (CTE) | 10-6 ℃ | ≤1.2 |
| abun cikin toka | % | ≤0.2 |
| Halayen Halayen Nonuwa (4TPI) | ||
| Yawan yawa | g/cm3 | 1.78-1.84 |
| Ƙarfin mai juzu'i | MPa | ≥22.0 |
| Young' Modul | GPA | ≤18.0 |
| Takamaiman Juriya | µΩm | 3.4 zuwa 3.8 |
| (CTE) | 10-6 ℃ | ≤1.0 |
| abun cikin toka | % | ≤0.2 |