RP 450mm Graphite Electrode
Babban albarkatun kasa na graphite lantarki samar da man fetur coke.Za a iya ƙara ƙaramin adadin coke na kwalta zuwa lantarki na graphite na yau da kullun.
Babban albarkatun kasa irin wannanRP 450mm Graphite Electrodeman fetur koke.Za a iya ƙara ƙaramin adadin coke na kwalta zuwa lantarki na graphite na yau da kullun.Abubuwan da ke cikin sulfur na man coke da kwalta coke kada su wuce 0.5%.Ana kuma buƙatar coke ɗin allura don samar da lantarki mai ƙarfi ko ultra high power graphite electrodes.Bugu da ƙari, yana da fitattun siffofi na ƙananan tsarin, mai kyau lantarki da kuma thermal watsin, karfi hadawan abu da iskar shaka juriya, lalata juriya, low resistivity, high halin yanzu load juriya, low price da kuma high kudin tasiri.Ana amfani da shi sosai wajen narke karafa daban-daban.
Karfe babban mabukaci ne a masana'antar carbon, kuma graphite electrode ya zama mabuɗin zinare don masana'antar carbon don shiga filin ƙarfe.
Kwatanta Bayanin Fasaha don RP Graphite Electrode 18 ″ | ||
Electrode | ||
Abu | Naúrar | Specific mai bayarwa |
Halayen Halayen Sanda | ||
Diamita na Suna | mm | 450 |
Max Diamita | mm | 460 |
Min Diamita | mm | 454 |
Tsawon Suna | mm | 1800-2400 |
Matsakaicin Tsayin | mm | 1900-2500 |
Min Tsawon | mm | 1700-2300 |
Yawan yawa | g/cm3 | 1.55-1.63 |
Ƙarfin mai juzu'i | MPa | ≥8.5 |
Young' Modul | GPA | ≤9.3 |
Takamaiman Juriya | µΩm | 7.5-8.5 |
Matsakaicin yawa na yanzu | KA/cm2 | 13-17 |
Ƙarfin ɗauka na Yanzu | A | 22000-27000 |
(CTE) | 10-6 ℃ | ≤2.4 |
abun cikin toka | % | ≤0.3 |
Halayen Halayen Nono (4TPI/3TPI) | ||
Yawan yawa | g/cm3 | 1.74 |
Ƙarfin mai juzu'i | MPa | ≥16.0 |
Young' Modul | GPA | ≤13.0 |
Takamaiman Juriya | µΩm | 5.8-6.5 |
(CTE) | 10-6 ℃ | ≤2.0 |
abun cikin toka | % | ≤0.3 |