500mm Graphite Electrodes tare da Nonuwa
Rashin juriya na iskar oxygen yana da kyau, kuma ana rage yawan amfani da lantarki.Zaɓaɓɓen kayan albarkatun ƙasa masu inganci, graphitization a babban zafin jiki, ƙarancin abun ciki na ƙazanta
A 500mmRP graphite lantarki samar da China Hexi Carbon Co., Ltd. yana da low resistivity, mai kyau conductivity, high thermal hira kudi, high kumburi yadda ya dace, hadawan abu da iskar shaka juriya da kuma low electrode amfani.Suna amfani da kayan albarkatun ƙasa masu inganci, tare da ƙarancin abun ciki na ƙazanta.Babban ma'aunin juriya na zafin zafi yana da kyau kwarai, wanda zai iya daidaitawa da yanayin narkewa daban-daban, kuma raunin raunin karaya yana da ƙasa.Ana sarrafa su da kayan aikin injin mai sauri, tare da kyakkyawan kwanciyar hankali na inji.Kayan aikin injin gabaɗaya kuma na iya kammala sarrafa na'urar, amma shirye-shiryen yankan ya bambanta da na'urar jan ƙarfe.Su ne carbon electrodes, saboda kyakkyawan aiki na graphite, don haka a cikin aikin fitarwa zai iya adana lokaci mai yawa, wanda shine daya daga cikin dalilan amfani da graphite a matsayin electrode.Ana iya amfani da su ko'ina don yin wutar lantarki tanderun ƙarfe, silicon masana'antu, gilashin ma'adini, corundum da sauran masana'antu.
Kwatanta Bayanin Fasaha don RP Graphite Electrode 20 ″ | ||
Electrode | ||
Abu | Naúrar | Specific mai bayarwa |
Halayen Halayen Sanda | ||
Diamita na Suna | mm | 500 |
Max Diamita | mm | 511 |
Min Diamita | mm | 505 |
Tsawon Suna | mm | 1800-2400 |
Matsakaicin Tsayin | mm | 1900-2500 |
Min Tsawon | mm | 1700-2300 |
Yawan yawa | g/cm3 | 1.55-1.63 |
Ƙarfin mai juzu'i | MPa | ≥8.5 |
Young' Modul | GPA | ≤9.3 |
Takamaiman Juriya | µΩm | 7.5-8.5 |
Matsakaicin yawa na yanzu | KA/cm2 | 13-16 |
Ƙarfin ɗauka na Yanzu | A | 25000-32000 |
(CTE) | 10-6 ℃ | ≤2.4 |
abun cikin toka | % | ≤0.3 |
Halayen Halayen Nono (4TPI/3TPI) | ||
Yawan yawa | g/cm3 | 1.74 |
Ƙarfin mai juzu'i | MPa | ≥16.0 |
Young' Modul | GPA | ≤13.0 |
Takamaiman Juriya | µΩm | 5.8-6.5 |
(CTE) | 10-6 ℃ | ≤2.0 |
abun cikin toka | % | ≤0.3 |